evaluation of the interfacial bond properties between carbon phenolic and glass phenolic composites

  • 출판일1999.03
  • 저자
  • 서지사항
  • 등록일 2016.11.02
  • 조회수 364
the effects of moisture and surface finish on the mechanical and physical properties of the interfacial bond between the carbon/phenolic (c/p) and glass/phenolic (g/p) composite materials are presented in this paper. four flat panel laminates were fabricated using the c/p and g/p materials. of the four laminates, one panel was fabricated in which the c/p and g/p materials were cured simultaneously. it was identified as the cocure. the remaining laminates were processed with an initial simultaneous cure of the three c/p billets. two surface finishes, one on each half, were applied to the top surface. prior to the application and cure of the g/p material to the machined surface of the three c/p panels, each was subjected to specific environmental conditioning. types of conditioning included' nominal fabrication environment, a prescribed drying cycle, and a total immersion in water at 71 degrees c
이전글 다음글 목록